Emulsion-based latex aerosol paint

ABSTRACT

An emulsion-based latex aerosol paint comprises 5-50 weight percent of one or more hydrocarbon solvents, 0.05-10 weight percent of a surfactants with a Hydrophilic-Lipophilic Balance value of 4-10, 10-70 weight percent of a water-based coating emulsified into a mixture of the one or more solvents and the one or more surfactants. The emulsion-based latex aerosol paint may be additionally charged with a hydrocarbon propellant at a level of 5 to 50 weight percent. The hydrocarbon propellant may be selected from propane, butane, isobutene and mixtures thereof. A method of making an emulsion-based latex aerosol paint comprises providing one or more aliphatic solvents, adding one or more surfactants to the one or more aliphatic solvents to provide a solvent/surfactant mixture, adding a water-based coating to the solvent/surfactant mixture and emulsifying the water based coating in the solvent surfactant mixture to provide a water-based coating emulsion, and placing the water-based coating emulsion in a delivery system utilizing a hydrocarbon propellant.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims benefit of pending U.S. Provisional Application No. 62/310,451 filed on Mar. 18, 2016 and pending U.S. Provisional Application No. 62/314,467 filed on Mar. 29, 2016, the disclosures of which are incorporated by reference herein.

BACKGROUND OF THE INVENTION

The invention relates to aerosol coatings, particularly to an aerosol paint product. Even more particularly, the present invention relates to an aerosol latex paint and a method of manufacturing the same utilizing the same base paint as existing architectural products.

The use of paint in architectural applications is well known. Paints for these applications may be divided into oil-based paints and water-based or “latex” paints. These paints may be further divided into paints for exterior applications and those for interior applications. Architectural paint for interior applications is frequently water-based or latex paint, due to the ease of use and the fact that clean up requires water rather than mineral spirits or other organic solvents.

The use of water as a solvent however, has previously made the use of latex paint incompatible with most aerosol spray applications, due to the insolubility of the hydrocarbon propellants typically used in an aerosol spray paint application, such as propane, butane, or isobutene, in water. The use of partially water soluble gasses such as dimethyl ether is known in some limited aerosol applications, however when dimethyl ether is used with latex polymers the gas penetrates and swells the micelle resulting in a highly viscous non-sprayable gel.

It has been known to use water emulsified into a solvent based solution coating in ground marking/striping paint in the past. In such applications, water serves only as filler for cost reduction and does not involve a fully formulated, water-based coating emulsified into a carrier solvent. When water is added to a solvent-based coating it may introduce many problems such as: polymer insolubility, long dry times, poor film properties, high VOC, etc.

Therefore, there is a need for an aerosol latex paint in which a water-based coating is emulsified into a carefully chosen, controlled blend of solvents such that one is able to maintain the original properties and advantages of a modern latex coating. Such a product would provide an excellent touch-up tool over brushed or rolled architectural paint as well as a means to spray a latex coating without the use of bulky and expensive equipment.

BRIEF SUMMARY OF THE INVENTION

It is therefore, an aspect of the present invention to provide a latex aerosol paint.

In general, the present invention allows hydrocarbon-based propellants to be used with a water-based coating by providing an emulsion of a water-based coating and organic solvent (water in oil) into which hydrocarbon propellant can easily dissolve. While prior hydrocarbon propellants, such as propane/butane, are not soluble enough in water to function as a viable aerosol propellant, nor can propane/butane be emulsified directly into water, the use of the present emulsion of a water-based coating and organic solvent permits the hydrocarbon solvent to be used to create an aerosol latex paint.

The emulsion-based latex aerosol paint comprises 5 percent-50 percent by weight of one or more hydrocarbon solvents, 0.05 percent and 10 percent by weight of a surfactants with a Hydrophilic-Lipophilic Balance value of 4-10, 10 percent and 70 percent by weight of a water-based coating emulsified into a mixture of the one or more solvents and the one or more surfactants. The emulsion-based latex aerosol paint may be additionally charged with a hydrocarbon propellant at a level of 5 to 50 percent by weight. The hydrocarbon propellant may be selected from propane, butane, isobutene, and mixtures thereof.

The claimed invention also includes a method of making an emulsion-based latex aerosol paint. The method comprises providing one or more hydrocarbon solvents, adding one or more surfactants to the one or more hydrocarbon solvents to provide a solvent/surfactant mixture, adding water-based coating to the solvent/surfactant mixture and emulsifying the water-based coating in the solvent surfactant mixture to provide a water-based coating emulsion, and placing the water-based coating emulsion in a delivery system utilizing a hydrocarbon propellant.

In the present invention, one or more hydrocarbon solvents are selected so that the resulting evaporation profile approximates the evaporation profile of the water-based paint to be used. A surfactant with an HLB (Hydrophilic-Lipophilic Balance) value of between 4-10 is included in the solvent mixture. The chosen water-based coating can then be emulsified into the solvent/surfactant mixture under agitation at a level between 10 percent and 70 percent by weight. The resulting emulsion may then be placed into an aerosol can and charged with hydrocarbon propellant at a level of 5 percent to 50 percent by weight.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed toward an emulsion-based latex aerosol paint. The following examples should not be viewed as limiting the scope of the invention. The claims will serve to define the inventions.

In one embodiment, the invention may include the selection of an aliphatic solvent or a blend thereof that most closely matches the evaporation profile of the water-based paint that is to be emulsified at a usage level between 5 to 50 percent by weight. In one particular embodiment, the aliphatic solvent may be present at a level of 30 to 45 percent by weight. In one other particular embodiment the aliphatic solvent may be present at a concentration of approximately 35 percent by weight.

The appropriate surfactants with an HLB (Hydrophilic-Lipophilic Balance) value of between 4-10 are included in the solvent mixture. The surfactant usage level may be between 0.05 percent and 10 percent by weight. In some examples, this surfactant or emulsifier is present at a concentration of 0.05 to 3 percent by weight. In one particular embodiment, this surfactant is present at a concentration of approximately 1 percent by weight.

The chosen water-based coating can then be emulsified into the solvent/surfactant mixture under agitation at a level between 10 percent and 70 percent by weight. The resulting emulsion is then placed into an aerosol can and charged with hydrocarbon propellant at a level of 5 percent to 50 percent by weight or volume. The hydrocarbon propellant may consist of a propane/butane or propane/butane/isobutene blend.

The one or more hydrocarbon solvents may be aliphatic hydrocarbons, aromatic hydrocarbons, or a mixture thereof. Acceptable hydrocarbon solvents include those comprising C-5 to C-20 alkanes such as pentane, hexane, heptane, octane, and related hydrocarbons including their related isomers and mixtures thereof In some embodiments, the hydrocarbon solvent is a mixture of aliphatic and/or aromatic hydrocarbons such as Varnish Makers' & Painters' (VM & P) Naphtha or mineral spirits. Mineral spirits are petroleum distillates and may contain, for example, hexane, approximately 65 percent or more C10 or higher hydrocarbons and up to 25 percent C-7 to C-12 aromatic hydrocarbons. VM & P Naphtha is a mixture of petroleum distillates, chiefly pentanes and hexanes. Supplemental n-hexane may also be added to control the evaporation profile of the composition upon application, as provided more fully below.

As stated above, the present invention includes one or more hydrocarbon solvents that are selected so that the resulting evaporation profile approximates the evaporation profile of the water-based paint to be used. In one embodiment, the evaporation profile may be measured by the following method. The evaporation rate of water and a solvent is determined relative to the evaporation rate of n-butyl acetate. The evaporation rate of n-butyl acetate is assigned a value of 1. The amount of each component in the formulation is divided by its relative evaporation rate to obtain a value for each component. Optimally, the value for water is greater than the value for the solvent(s). For example, in a composition containing 40 percent total water, 5 percent Mineral Spirits and 10 percent VM & P Naphtha, the calculations would be made as follows:

Water: 40/0.36=111.2

Mineral Spirits: 5/0.12=41.6

VM & P Naphtha: 10/1.6=6.25

Further adjustments in the composition may be necessary to account for factors such as product viscosity.

In various embodiments, the evaporation profile of the solvent or solvent blend used may be within 40 percent of the evaporation profile of the water-based paint. In other embodiments, the evaporation profile of the solvent or solvent blend used may be within 10 percent of the evaporation profile of the water-based paint. In further embodiments, the evaporation profile of the solvent or solvent blend used may be within 5 percent of the evaporation profile of the water-based paint. In still other embodiments, the evaporation profile of the solvent or solvent blend used may be within 2 percent of the evaporation profile of the water-based paint.

Suitable solvents include VM & P Naphtha, mineral spirits, pentane, hexane, heptane, octane, and other hydrocarbons ranging from C-5 to C-20 and their related isomers and mixtures thereof In some embodiments, the aliphatic solvent may be VM & P Naphtha, present in the composition at a concentration up to about 40 percent by weight or volume. In one example, VM & P Naphtha is present at a concentration of between about 4.5 percent and about 17 percent by weight or by volume. In addition or in the alternative, mineral spirits may be present in the composition at a concentration up to about 20 percent by weight or volume, such as between about 5 percent and about 20 percent by weight or by volume. In other examples, the total solvent concentration is between 30 and 45 percent by weight. In such an example, the solvent may comprise 0 to 20 percent by weight mineral spirits, 0 to 40 percent by weight VM &P Naphtha, and 0 to 20 percent by weight n-hexane. In one particular example, the solvent may comprise 10 percent by weight mineral spirits, 20 percent by weight VM &P Naphtha, and 5 percent by weight n-hexane. In another particular example, the solvent consists of 10 percent by weight mineral spirits, 20 percent by weight VM &P Naphtha, and 5 percent by weight n-hexane.

The composition also includes one or more surfactants with an HLB value of between 4-10, at a concentration between 0.05 percent and 10 percent by weight or volume. In some examples, the surfactant is present at a concentration between 0.05 percent and 3 percent by weight or volume. Examples of suitable surfactants include but are not limited to Tergitol NP-4, Schercodine S, Amadol 511 and Arquad 2C-75.

Thixotropic agents such as bentonite clays or similar minerals may also be included. Examples include Garamite 1958, Bentone SD-1, and BYK411.

Examples of the present invention were mixed and test sprayed as shown in Table 1.

TABLE 1 Bulk Paint Formula Results of Formula Promar 200 Flat - 40% Bulk Paint, 16% VM&P Good color match, Stability Practical Biege & Naphtha, 17% Water, 1% Tergitol 4 Months Kilim Biege NP-4, 0.75% Garamite 1958, 0.25% BYK411 Promar 200 - Practical 40% Bulk Paint, 16% VM&P No Color Match attempted, Beige Naphtha, 17% water, 1% Tergitol, Stability 10 Months and still 0.75% Schercodine P, 0.25% going (sprayed once a BYK411 month) Promar 400 Flat - 40% Bulk Paint, 15.25% Mineral Stability 4 months until cans Practical Biege Spirits, 17% Water, 1.25% Amadol empty, Color match 511, 1.25% Arquad 2C-75, 0.25% passable BYK411 Promar 400 Low 40% Bulk Paint, 17% Water, 16% Good Color Match, Stability Sheen - Nomadic VM&P Naphtha, 1% Tergitol NP-4, 5 months Desert, A New Gray, 0.75% Garamite 1958, 0.25% Agreeable Gray, BYK411 Balanced Beige, Tony Taupe Promar 400 Gloss - 40% Bulk Paint, 14.25% Mineral No Stability Data. White Spirits, 17% Water, 2% Tergitol NP-4, 0.25% Garamite 1958, 0.25% BYK411 Promar 200 Semi- 32% Bulk Paint, 16% Mineral Stability 2 Months/ Gloss - Practical Biege Spirits, 17.75% Water, 6.5% VM&P Separation(bubbling), Lost Naphtha, 2.5 Tergitol NP-4, 0.25% Gloss over time BYK411 Duration Int. Satin - 32% Bulk Paint, 16% Mineral Good color match, Stability Practical Biege Spirits, 17.75% Water, 6.5% VM&P 4 months/ Naphtha, 1.25 Tergitol NP-4, 1.25% separation(bubbling), Kept Amadol 511, 0.25% BYK411 Gloss Duration Int. Matte - 32% Bulk Paint, 16% Mineral Good color match, Stability Practical Biege Spirits, 17.75% Water, 6.5% VM&P 4 months/separation Naphtha, 1.25 Tergitol NP-4, 1.25% (bubbling) Amadol 511, 0.25% BYK411 Pulte Homes - Natural 40% Bulk Paint, 16% VM&P Good color match, used in Choice Naphtha, 17% Water, 1% Tergitol field testing NP-4, 0.75% Garamite 1958, 0.25% BYK411 Pulte Homes - Natural 32% Bulk Paint, 22% Mineral Good color match, Stability Choice Spirits, 18.75% Water, 1.25% 7 months Tergitol NP-4, 0.75% Garamite 1958, 0.25% BYK411 Super Paint Ext. Satin - 32% Bulk Paint, 19.25% Mineral Stability 2 Months Oven, Practical Biege & Spirits, 21% Water, 1.25% Tergitol Passable color match Adriatic Sea NP-4, 0.75% Garamite 1958, 0.50% Schercodine S, 0.25% BYK411 Emerald Int. Satin - 32% Bulk Paint, 18% Mineral Stability 9 Months Oven/ Practical Biege Spirits, 22.75% Water, 1.25% Viscosity increase/Very Tergitol NP-4, 0.75% Garamite Textured, Lost Gloss over 1958, 0.25% BYK411 time, Passable color match Resilience Gloss - 32% Bulk Paint, 18.75% Mineral Good color match, Stability Practical Biege Spirits, 22% Water, 1.25% Tergitol 4 months until separation NP-4, 0.75% Garamite 1958, 0.25% due to viscosity increase, BYK411 steady gloss throughout, showing texturing from month 3 on Resilience Satin - 32% Bulk Paint, 18.75% Mineral No Stability Data, Tricorn Black Spirits, 22% Water, 1.25% Tergitol Troubleshooting Gloss NP-4, 0.75% Garamite 1958, 0.25% Reduction, Good Spray BYK411 otherwise. Super Paint Int. Flat - 40% Bulk Paint, 15% Mineral Stability 2 Months Oven/ Practical Biege Spirits, 18% Water, 1.25% Amadol 511, 0.50% Arquad 2C-75, 0.25% BYK411 Super Paint Ext. Flat - 40% Bulk Paint, 14.25% Mineral Stability 9 Months until Practical Biege Spirits, 18% Water, 1.25% Amadol empty, good color match 511, 1.25% Arquad 2C-75, 0.25% BYK411 Super Paint Int. Semi- 40% Bulk Paint, 15.25% Mineral 1 month of Stability/ Gloss - Practical Biege Spirits, 17% Water, 1.25% Amadol 511, 0.75% Garamite 1958, 0.50% Schercodine S, 0.25% BYK411 Promar 400 Semi- 40% Bulk Paint, 18% Mineral 1 Week on Stability/ Gloss - Practical Biege Spirits, 15% Water, 1.25% Amadol Separation 511, 0.50% Arquad 2C-75, 0.25% BYK411 Promar 200 Satin - 40% Bulk Paint, 15.25% Mineral Good Color Match, Stability Practical Biege Spirits, 17% Water, 1.25% Tergitol 3 Months/ NP-4, 0.75% Garamite 1958, 0.50% Arquad 2C-75, 0.25% BYK411 Promar 400 Egg Shell - 40% Bulk Paint, 15.75% Mineral Stability 2 Months/Visc. Practical Biege Spirits, 17% Water, 1.25 Tergitol Increase/Texturing Passable NP-4, 0.75% Garamite 1958, 0.25% color match slightly darker BYK411 Emerald Ext. Satin - 32% Bulk Paint, 16% Mineral Good Color Match, Stability Practical Biege Spirits, 17.75% Water, 6.5% VM&P 1 Month/Separation/ Naphtha, 2.5% Tergitol NP-4, Bubbling 0.25% BYK411 Duration Ext. Flat - 32% Bulk Paint, 16% Mineral UV Test (White), Stability 1 White & Practical Spirits, 17.75% Water, 6.5% VM&P Month/Separation Beige Naphtha, 1.25% Tergitol NP-4, (Practical Beige) 1.25% Amadol 511, 0.25% BYK411 Emerald Ext. Flat - 32% Bulk Paint, 16% Mineral UV Test, No Stability Data White Spirits, 17.75% Water, 6.5% VM&P Naphtha, 2.5% Tergitol NP-4, 0.25% BYK411 Sherscrub Flat - Panda 40% Bulk Paint, 17% Water, 16% Good color match, used in White & Kilim Beige VM&P Naphtha, 1% Tergitol NP-4, field testing 0.75% Garamite 1958, 0.25% BYK411 Pro-Classic Semi 32% Bulk Paint, 18.25% Mineral Good color match, Stability Gloss - White Spirits, 21% water, 2% Tergitol NP- 4 months 4, 0.25% Garamite 1958, 0.25% Byk411, 1% Texanol Pro Classic 32% Bulk Paint, 18% Mineral 4 week stability then (Waterbased Alkyd) Spirits, 21% water, 2% Tergitol NP- showing kickout Semi-Gloss - White 4, 0.50% Garamite 1958, 0.25% Byk411, 1% Texanol, 0.10% Cobalt Drier Eminence Flat Ceiling 40% Bulk Paint, 15.75% Mineral 3 months in stability, Paint - White Spirits, 17% Water, 1.25 Tergitol coverage slightly too light NP-4, 0.75% Garamite 1958, 0.25% and spray too misty with BYK411 vertical valve and actuator Eminence Flat Ceiling 50% Bulk Paint, 10.50% Mineral No Stability Data, Used for Paint - White Spirits, 12% Water, 1.25% Tergitol field test. Better spray and NP-4, 1% Garamite 1958, 0.25% less mist than above formula BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P 2 months in stability, great Kilim Beige Naphtha, 5% Mineral Spirits, 11% color match, used in Water, 3% Tergitol NP-4, 1.25% marketing team demo Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Cool Platinum Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Nomadic Desert Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Agreeable Gray Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Swiss Coffee Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painers Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Macadamia Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Desert Fawn Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Sienna Sand Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Basketweave Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Botany Beige Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Lulled Beige Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Antique White Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 50% Bulk Paint, 12% VM&P Good color match, 2 months Bone White Naphtha, 5% Mineral Spirits, 11% in stability, showing Water, 3% Tergitol NP-4, 1.25% viscosity increase Bentone SD-1, 0.75% BYK411 Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Cool Platinum Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Nomadic Desert Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Agreeable Gray Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% bentone sd-1, 0.25% byk411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Swiss Coffee Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painers Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Macadamia Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Desert Fawn Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Sienna Sand Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Basketweave Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Botany Beige Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Lulled Beige Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Antique White Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Flat - 45% Bulk Paint, 17% VM&P Good color match, 1 months Bone White Naphtha, 5% Mineral Spirits, 3% in stability, showing Tergitol NP-4, 1% Garamite 1958, viscosity increase 0.50% Bentone SD-1, 0.25% BYK 411, 11.25% water Painters Edge Egg 45% Bulk Paint, 13 VM&P Good color match, 2 months Shell - Kilim Beige Naphtha, 7% Mineral Spirits, 12% in stability, showing water, 3% Tergitol NP-4, 1.25% viscosity increase, still Bentone SD-1, 0.75% BYK411, 1% spraying as of Jan. 4, 2016 Texanol All Surface - Tricorn 40% Bulk Paint, 15% Mineral 5 weeks stability still Black Spirits, 18% Water, 1% Tergitol spraying, used for a field NP-4, 0.75% Garamite 1958, 0.25% test BYK411 All Surface - Tricorn 50% Bulk Paint, 12.5% Mineral 5 weeks stability still Black Spirits, 4.5% VM&P Naphtha, 16% spraying, used for a field Water, 1% Tergitol NP-4, 0.75% test Garamite 1958, 0.25% BYK411

In another example of the invention, higher solvent levels and lower propellant levels were used. The viscosity of a water in oil emulsion is primarily controlled by the ratio of water phase to oil phase. As more water is added, the viscosity increases. While commercial products of this type have evolved to contain fewer organic compounds and more water, it has been advantageously found that when modern latex paint is emulsified into an aerosol at higher solvent levels, those higher solvent levels allow for a lower viscosity product. In turn, this will provide a finer mister spray, a more uniform coating, and a better user experience than a similar system with less solvents. In this example, the solvent level is between 30 and 45 weight percent of the composition. In one particular example, the composition is approximately 35 percent by weight solvent. Additionally, the inclusion of hexane as a supplemental component of the solvent phase, in addition to the hexane normally present in mineral spirits or VM & P Naphtha, can allow for enhanced control of the evaporation profile to maintain an ideal viscosity through the drying process.

Lower solvent level aerosols generally result in poor compatibility with semi-gloss and gloss paint. The reduced propellant level of the current example allows for the aerosol to be compatible with higher gloss sheens such as semi-gloss and gloss paints. When a water in oil emulsion is sprayed, the system is in a state of dynamic equilibrium in which water and solvent are evaporating concurrently. As previously mentioned, the viscosity is a function of the water to oil ratio and thus it will continue to change through the drying processes. Reducing the amount of hydrocarbon propellant, which immediately volatilizes, allows for the other solvents which have a slower rate of evaporation to remain in the film longer. This provides for better flow and leveling of the coating, which results in a smoother film with a better gloss response. In one example, the hydrocarbon propellant level is between 5 and 20 percent of the composition. In another example, the hydrocarbon propellant is present at a concentration of 15 percent by weight or less.

These examples of the present invention were mixed and test sprayed as shown in Tables 2 and 3.

TABLE 2 HGTV Home Infinity by Sherwin Williams - Flat Sheen Weight % Results of Formula Bulk Paint 35 Good color match, Water 14 Heat stability good @ VM&P Naphtha 18.75 1 month. Mineral Spirts 10 Hexane 5 Tergitol NP4 2 BYK 411 0.25 Propane Butane Propellant Blend 15

TABLE 3 HGTV Home Infinity by Sherwin Williams - Satin Sheen Weight % Results of Formula Bulk Paint 35 Good color match, Water 14 Heat stability good VM&P Naphtha 17.75 @ 1 month. Texanol 1 Mineral Spirts 10 Hexane 5 Tergitol NP4 2 BYK 411 0.25 Propane Butane Propellant Blend 15

Based upon the foregoing disclosure, it should now be apparent that the emulsion-based latex aerosol paint will carry out the aspects set forth hereinabove. It is, therefore, to be understood that any variations evident fall within the scope of the claimed invention and thus, the selection of specific component elements can be determined without departing from the spirit of the invention herein disclosed and described. 

What is claimed is:
 1. An emulsion-based latex aerosol paint comprising: 25 percent to 45 percent by weight water-based coating emulsion; 5 percent to 20 percent by weight water; 30 percent-45 percent by weight of one or more hydrocarbon solvents; 0.05 percent-10 percent by weight of one or more surfactants with a Hydrophilic-Lipophilic Balance value of 4-10; and 10 percent-20 percent by weight of a hydrocarbon propellant.
 2. The emulsion-based latex aerosol paint of claim 1, comprising 15 percent by weight hydrocarbon propellant.
 3. The emulsion-based latex aerosol paint of claim 2, wherein hydrocarbon propellant is selected from propane, butane, isobutene and mixtures thereof.
 4. The emulsion-based latex aerosol paint of claim 2, wherein the one or more hydrocarbon solvents are selected from one or more aliphatic hydrocarbons, one or more aromatic hydrocarbons, and mixtures thereof
 5. The emulsion-based latex aerosol paint of claim 4, wherein the one or more hydrocarbon solvents comprise C-5 to C-20 alkanes.
 6. The emulsion-based latex aerosol paint of claim 4, wherein the one or more hydrocarbon solvents are selected from VM & P Naphtha, mineral spirits, n-hexane, and mixtures thereof
 7. The emulsion-based latex aerosol paint of claim 6, comprising: 35 percent by weight water-based coating emulsion comprising latex paint; 14 percent by weight water; 35 percent by weight of one or more hydrocarbon solvents; 1 percent by weight of one or more surfactants with a Hydrophilic-Lipophilic Balance value of 4-10; and 15 percent by weight of a hydrocarbon propellant.
 8. The emulsion-based latex aerosol paint of claim 7, wherein the one or more hydrocarbon solvents comprise 10 weight percent mineral spirits, 20 weight percent VM & P Naphtha and 5 weight percent n-hexane.
 9. The emulsion-based latex aerosol paint of claim 1, comprising: 35 percent by weight water-based coating emulsion comprising latex paint; 14 percent by weight water; 35 percent by weight of one or more hydrocarbon solvents; 1 percent by weight of one or more surfactants with a Hydrophilic-Lipophilic Balance value of 4-10; and 15 percent by weight of a hydrocarbon propellant.
 10. A method of making an emulsion-based latex aerosol paint, the method comprising: providing one or more hydrocarbon solvents; adding one or more surfactants to the one or more aliphatic solvents to provide a solvent/surfactant mixture; adding a water-based coating to the solvent/surfactant mixture and emulsifying the water based coating in the solvent surfactant mixture to provide a water-based coating emulsion; placing the water-based coating emulsion in a delivery system utilizing a hydrocarbon propellant to provide an emulsion-based latex aerosol paint; wherein the emulsion-based latex aerosol paint comprises 25 percent to 45 percent by weight latex paint, 5 percent to 20 percent by weight water, 30 percent-45 percent by weight of one or more hydrocarbon solvents, 0.05 percent-10 percent by weight of one or more surfactants with a Hydrophilic-Lipophilic Balance value of 4-10, and 10 percent to 20 percent by weight of a hydrocarbon propellant.
 11. The method of claim 10, wherein the delivery system is an aerosol can.
 12. The method of claim 10, wherein the hydrocarbon propellant is selected from propane, butane, isobutene, and mixtures thereof.
 13. The method of claim 10, wherein the one or more hydrocarbon solvents are present in the water-based coating emulsion at a concentration of 35 percent by weight.
 14. The method of claim 13, wherein the one or more hydrocarbon solvents are selected from one or more aliphatic hydrocarbons, one or more aromatic hydrocarbons, and mixtures thereof.
 15. The method of claim 14, wherein the one or more hydrocarbon solvents comprise C-5 to C-20 alkanes.
 16. The method of claim 14, wherein the one or more hydrocarbon solvents are selected from VM & P Naphtha, mineral spirits, n-hexane, and mixtures thereof
 17. The method of claim 16, wherein the one or more surfactants are present in the water-based coating emulsion at a concentration of 0.05 percent to 3 percent by weight.
 18. The method of claim 17, wherein the latex paint is present in the water-based coating emulsion at a concentration of 35 percent by weight.
 19. The method of claim 10, wherein the emulsion-based latex aerosol paint comprises: 35 percent by weight water-based coating emulsion comprising latex paint; 14 percent by weight water; 35 percent by weight of one or more hydrocarbon solvents; 1 percent by weight of one or more surfactants with a Hydrophilic-Lipophilic Balance value of 4-10; and 15 percent by weight of a hydrocarbon propellant.
 20. The method of claim 19, wherein the one or more hydrocarbon solvents comprise 10 weight percent mineral spirits, 20 weight percent VM & P Naphtha and 5 weight percent n-hexane. 